Features: |
Stable Constant Expansion Coefficient |
Shape: |
Wire,Strip,Rod,Tube,Plate |
Alloy Type: |
Iron-nickel Alloy |
Raw Materials: |
NI48%，Fe Margin |
Executive Standard: |
ASTM，GOST |
Delivery State: |
Sosoloid |
Application: |
For Aviation,aerospace And Semiconductor |
Size: |
Negotiable |
Features: |
Stable Constant Expansion Coefficient |
Shape: |
Wire,Strip,Rod,Tube,Plate |
Alloy Type: |
Iron-nickel Alloy |
Raw Materials: |
NI48%，Fe Margin |
Executive Standard: |
ASTM，GOST |
Delivery State: |
Sosoloid |
Application: |
For Aviation,aerospace And Semiconductor |
Size: |
Negotiable |
KX NILO 48 Corrosion Resistant Alloy Light Rod On Expansion Alloy
Product Description and Application
NILO 48 is also known as the K94800, Pernifer 48, Alloy 48, 48HX (Russian).
NILO 48 has good comprehensive properties in the temperature range of -253 ~ 700℃, the yield strength below 650℃ ranks the first place in the deformation superalloy and has good property, including processing property and welding property. It can manufacture all kinds of parts with complex shapes and has been widely used in aerospace, nuclear energy, petroleum industry and extrusion mold in the above temperature range.
Process Performance and Requirements
Vacuum Induction Furnace(VIM) and Electroslag Remelting Furnace(ESR)
| Alloy | % | Ni | Fe | Mn | Si | C | Cr | P | S | Al |
| NILO 48 | Min | 48.00 | Bal | - | - | - | - | - | - | - |
| Max | Nominal | 0.80 | 0.30 | 0.05 | 0.25 | 0.025 | 0.03 | 0.10 |
| Density | 8.1g/cm3 |
| Fusing Temperature | 1450℃ |
| Alloy Grade | Sample Heat Treatment Institution |
Average coefficient of linear expansion α(10-6/ K) |
||
| 20～ 300 oC | 20～ 400 oC | 20～ 450 oC | ||
| NILO 48 | It is heated to 900±20 oC in hydrogen atmosphere, insulated lh, and cooled to less than 200 oC at a speed of no more than 5 oC/ min | 9.2～ 10.0 | 9.2～ 9.9 | ------- |
WireTensile Strength
| State Code | State | Tensile Strength/MPa |
| R | Soft | <590 |
| I | Hard | >820 |
Strip Tensile Strength
| State Code | State | Tensile Strength/MPa |
| R | Soft | <570 |
| I | Hard | >700 |
Professional Customization
| Cold-drawn Wire | ¢0.3~¢18mm(Delivery in rolls or trays) |
| Hot-Rolling Wire | ¢5.5~¢20mm(Delivery in rolls) |
| Strip | thickness 0.1~4.5*width 6~350mm(Supply in rolls or straight strips) |
| Smooth Forged Rod on a Lathe |
¢60~350mm,L800-2500mm
|
| Hot-rolled Burnishing | ¢20~80mm,L1000-5000mm |
| Cold Drawn and Burnishing | ¢2.5~18mm,L1000-8000mm |
| Seamless Tube | ¢1~275mm,wall thickness 0.2~30,L1000-8000mm |