Product Details
Place of Origin: China
Brand Name: KAIXIN
Certification: ISO9001:2015
Model Number: KX-Alloy605
Payment & Shipping Terms
Minimum Order Quantity: 200KG
Price: To negotiate
Packaging Details: Wooden Box, size as per guests request
Delivery Time: 45~60days
Payment Terms: T/T, L/C
Supply Ability: 50~80TONS per MONTH
Features: |
Excellent Stability And High Strength |
Shape: |
Wire, Strip, Rod, Tube, Plate |
Alloy Type: |
Nickel-based Deformed Superalloy |
Raw Materials: |
NI9-11%,CR19-21%,W14-16%,MO Rem |
Executive Standard: |
ASTM |
Delivery State: |
Sosoloid |
Application: |
Manufacture Engine Guide Blade, Turbine Outer Ring, Outer Wall, Swirler, Sealing Plate And Etc Parts |
Size: |
Negotiable |
Features: |
Excellent Stability And High Strength |
Shape: |
Wire, Strip, Rod, Tube, Plate |
Alloy Type: |
Nickel-based Deformed Superalloy |
Raw Materials: |
NI9-11%,CR19-21%,W14-16%,MO Rem |
Executive Standard: |
ASTM |
Delivery State: |
Sosoloid |
Application: |
Manufacture Engine Guide Blade, Turbine Outer Ring, Outer Wall, Swirler, Sealing Plate And Etc Parts |
Size: |
Negotiable |
KX GH5605 Uns Light Rod Plate Structural Operating Temperature Range For High Temperature Alloy
Product Description and Application
GH5605 is also known as L605,UNSR30605,GH605
GH5605 is a Co-Cr-Ni based solid solution enhanced deformation superalloy, its use temperature is below 1000℃. Cobalt-based superalloy GH5605 is a cobalt base alloy strengthened by solution of 20%Cr and 15%W(percent mass). It has medium durability and creep strength below 815℃, excellent oxidation resistance below 1 090℃, and satisfactory process properties such as forming and welding. It is a key material for aero engine, rocket engine, naval ship and industrial gas turbine. Its development and production status is one of the symbols on the metal materials development level in a country. It is used for manufacturing the high temperature parts of aero engine guide blade, turbine outer ring, outer wall, swirler and sealing plate.
Process Performance and Requirements
Vacuum Induction Furnace(VIM) and Electroslag Remelting Furnace(ESR)
| Composition | Fe | C | Si | Mn | P | S | Cr | Ni | W | More |
| Min | - | 0.05 | - | 1 | - | - | 19 | 9 | 14 | Co:Rem |
| Max | 3 | 0.15 | 0.4 | 2 | 0.04 | 0.03 | 21 | 11 | 16 |
| Density | p=9.13g/cm3 |
| Melting Temperature Range | 1330℃-1410℃ |
| Variety | Tensile Property in the Room Temperature |
Hardness HV |
815℃ Durability | Grain Size/Grade | Other properties | ||||
| MPa | MPa | MPa | MPa | t/h | % | ||||
| Middle Plate,Sheet,Strip | ≧890 | 370-550 | ≧35 | ≤290 | 165 | ≧24 | ≧10 | ≧2.5(1) | Bend |
|
Cold Hard Strip Grade A |
≧1500 | ≧1300 | ≧5 | 410-480 | --- | ---- | --- | ≧9 | Bend |
|
Cold Hard Strip Grade B |
≧1700 | ≧1500 | ≧3 | 485-560 | --- | --- | --- | ≧10 | Bend |
| Bar | ≧860 | ≧340 | ≧35 | ≤ 282 | 165 | ≧ 23 | ≧10 | ≧2(0) | --- |
| Ring | ≧860 | ≧310 | ≧30 | ≤ 248 | 165 | ≧ 24 | ≧10 | ≧2(0) | --- |
Professional Customization
| Cold-drawn Wire | ¢0.3~¢18mm(Delivery in rolls or trays) |
| Hot-Rolling Wire | ¢5.5~¢20mm(Delivery in rolls) |
| Strip | thickness 0.1~4.5*width 6~350mm(Supply in rolls or straight strips) |
| Smooth Forged Rod on a Lathe |
¢60~350mm,L800-2500mm |
| Hot-rolled Burnishing | ¢20~80mm,L1000-5000mm |
| Cold Drawn and Burnishing | ¢2.5~18mm,L1000-8000mm |
| Seamless Tube | ¢1~275mm,wall thickness 0.2~30,L1000-8000mm |