Product Details
Place of Origin: China
Brand Name: KAIXIN
Certification: ISO9001:2015
Model Number: KX-Alloy4099
Payment & Shipping Terms
Minimum Order Quantity: 200KG
Price: To negotiate
Packaging Details: Wooden Box, size as per guests request
Delivery Time: 45~60days
Payment Terms: T/T, L/C
Supply Ability: 50~80TONS per MONTH
Features: |
1000℃ Features: The Alloy Has A High Thermal Force, Can Be Used For A Long Time Below 900℃ And The Highest Working Temperature Can Reach 1000℃ |
Shape: |
Wire, Strip, Rod, Tube, Plate |
Alloy Type: |
Precipitate-hardened Nickel Based Alloy |
Raw Materials: |
NI Rem,CR 17-20%,CO 5-8% |
Executive Standard: |
GB/T1992，GOST |
Delivery State: |
Sosoloid |
Application: |
Used For Manufacturing Aircraft Engines, Processing Adjustable Nozzle Shells And Processing Cylinders |
Size: |
Negotiable |
Features: |
1000℃ Features: The Alloy Has A High Thermal Force, Can Be Used For A Long Time Below 900℃ And The Highest Working Temperature Can Reach 1000℃ |
Shape: |
Wire, Strip, Rod, Tube, Plate |
Alloy Type: |
Precipitate-hardened Nickel Based Alloy |
Raw Materials: |
NI Rem,CR 17-20%,CO 5-8% |
Executive Standard: |
GB/T1992，GOST |
Delivery State: |
Sosoloid |
Application: |
Used For Manufacturing Aircraft Engines, Processing Adjustable Nozzle Shells And Processing Cylinders |
Size: |
Negotiable |
KX GH4099 Light Rod Plate Structural Operating Temperature Range For High Temperature Alloy
Product Description and Application
GH4099 is also known as "P 693," "N" 68 manas ona (R) "n" (R)
GH4099 is a high alloying nickel-based aging alloy, which is strengthened with cobalt, tungsten, aluminum, titanium and etc elements, so that the alloy has a high thermal force, which can be used for a long time below 900℃and the highest working temperature can reach 1000℃. The alloy has stable microstructure and satisfactory performance in cold and hot processing and welding process, which is suitable for high temperature plate bearing welding structural parts such as aeroengine combustion chamber and afterburner. Large plate structural parts made of this alloy can be directly used after solution treatment without aging treatment.
Process Performance and Requirements
Vacuum Induction Furnace(VIM) and Electroslag Remelting Furnace(ESR)
|
Grade
|
C | Mn | Si | P | S | Ni | Cr | Ti | AI | CO | Fe | W | Mo | Mg | B | Ce |
| GH4099 |
≤ 0.08 |
≤ 0.4 |
≤ 0.5 |
≤ 0.015 |
≤ 0.015 |
Rem |
17.0 ~ 20.0 |
1.0 ~ 1.5 |
1.7 ~ 2.4 |
5.0 ~ 8.0 |
≤ 2.0 |
5.0 ~ 7.0 |
3.5 ~ 4.5 |
≤ 0.01 |
≤ 0.005 |
≤ 0.02 |
|
Test Temperature °C |
Heat Treatment or Condition |
Tensile Strength Mpa |
Elongation after breaking % |
| Room Temperature | Delivery State | ≤1130 | ≥35 |
| 900°C | Delivery status + time limitation | ≥295 | ≥23 |
| Recommended solution treatment institution: 1080~1140°C(maximum 1160°C), air cooling or rapid cooling; Aging treatment: 900±10°C, heat preservation for 5h, air cooling | |||
| Grade | Test State and Heat Treatment institution | Plate Thickness/mm |
Test Temperature /℃ |
Test Stress/MPa |
Test Time /h |
Elongation after breaking/% |
| GH4099 | Delivery State | 0.8－4.0 | 900 | 98 | ≧ 30 | ≧ 10 |
Professional Customization
| Cold-drawn Wire | ¢0.3~¢18mm(Delivery in rolls or trays) |
| Hot-Rolling Wire | ¢5.5~¢20mm(Delivery in rolls) |
| Strip | thickness 0.1~4.5*width 6~350mm(Supply in rolls or straight strips) |
| Smooth Forged Rod on a Lathe |
¢60~350mm,L800-2500mm |
| Hot-rolled Burnishing | ¢20~80mm,L1000-5000mm |
| Cold Drawn and Burnishing | ¢2.5~18mm,L1000-8000mm |
| Seamless Tube | ¢1~275mm,wall thickness 0.2~30,L1000-8000mm |